撸ZDP189 C11，字数字数字数

cifire2

前几天入的C11 ZDP189，蛋疼的原厂开刃，锋利度只能说可以，这么NB的钢开刃开成这样，我改刃的瑞士军刀直接就秒杀了，更别提手里的青纸钢啥的。这两天每天磨一个小时（怕花了所以比较慢），先不改原厂刃角，前半部分锋利了不少，后半部分靠刀根不好磨，还得继续撸。刃黑1000下肉块，上到8000目就很慢了，单用低目数的有达不到极致锋利。这个钢还真是费劲。


这是一老外的review，跟我感受相同。

Nice knife, but needs thining behind primary edge to get the most out of itsDan (NW Arkansas)        1/20/2014 10:21 PM
Out of the box this knife is so, so sharp. I found that the area behind the primary edge needs thinning. Because this is ZDP-189 , you better know how to freehand sharpen on a diamond stone or be good with a belt grinderer. After going through 8" x 3" diamond stones in 140, 300, 600 and 1,000 grit, I was able to thin out the area for about 1/4" behind the primary edge. Now this knife is as sharp, as any knife can be. And it will hold this edge longer than any other steel I know. However, with over 3% carbon and crazy amounts of other steel chemistry, it's extremely difficult to sharpen. Edge retention is excellent, but not unless you are prepared to do the work up front to get that edge thinned down. I don't know why Spyderco didn't do this at the factory, but they didn't. On the plus side it has an extremely strong lock and is very tight. Personally, I don't lke RC in the 65 range. I prefer 60 RC max. However, if you know how to fix the edge geometry, you will have a totally sick edge that will last a very long time.

abdc222

我觉着我的C11很锋利 也是ZDP189版本的     我是出厂状态直接上12000目磨

cifire2

abdc222 发表于 2014-2-27 13:31
我觉着我的C11很锋利 也是ZDP189版本的     我是出厂状态直接上12000目磨

我的一般般，不过得看跟什么比，我觉得我手上这把的锋利度对不起ZDP189，我想象中应该是可以劈头发的，实际达不到。

我一开始直接上8000目，不行，得打薄，尽量不改刃角，否则工作量大了。

abdc222

cifire2 发表于 2014-2-27 13:37
我的一般般，不过得看跟什么比，我觉得我手上这把的锋利度对不起ZDP189，我想象中应该是可以劈头发的，实 ...

我直接上12000目  我不舍得拔头发  割一根腿毛下来 一刀断开

花言巧语

ZDP189的C11多少一把啊

拉不达

碳含量3%，铬含量20%，钼含量1.3%，钨含量1.5%，钒含量0.1%。

碳含量堪比生铁啊。
问个问题，这不锈钢脆不？